          TR-1010 Unsaturated polyester Resin (modified)

          2023-11-07

          1. Features and main uses:

          Tianrun TR-1010 is an unsaturated polyester resin (modified) with phthalic anhydride and standard diols as the main raw materials, which has been dissolved in styrene. With low viscosity and high reactivity, light resistance, water resistance, weather resistance is particularly good. It has high mechanical properties and hardness after curing. It is especially suitable for FRP products with high transparency, high light resistance, high water resistance and high weather resistance.


          2. Technical specifications of liquid resin (25℃) :


          Item



          Unit



          Test index



          Test method



          Appearance



          ---



          Transparent water white liquid



          GB/T8237.6.1.1



          Viscosity



          Pa·s



          0.16-0.20



          GB/T 7193-2008



          Acid Number



          mgKOH/g



          14-25



          GB/T 2895-2008



          Gel Time



          Min(25℃)



          7-9



          GB/T 7193-2008



          Stability



          H(80℃)



          ≥24



          GB/T 7193-2008


          Note: Gel time test at 25℃ : Water bath at 25℃, 50g resin added 1ml curing agent M-55 and 2ml accelerator RCA.


          3. Physical properties of the casting body (for reference only) :


          Item



          Unit



          Test index



          Test method



           



           



          Casting body



           



          Tensile strength



          MPa



          ≥68



          GB/T2567-2008



          Tensile modulus of elasticity



          MPa



          ≥3600



          GB/T2567-2008



          Elongation at break



          %



          ≥2.0



          GB/T2567-2008



          Bending strength



          MPa



          ≥68



          GB/T2567-2008



          Flexural elastic modulus



          MPa



          ≥4100



          GB/T2567-2008



          Thermal deformation temperature





          ≥85



          GB/T1634-2004



          Bacor hardness



          ---



          ≥48



          GB/T3854-2005


          Note: (1) Casting system sample method according to GB/T8237-2005 execution; Temperature 25℃, curing system: accelerator RCA 1.0%, curing agent M-50 1.5%.

                    (2) Curing after casting: room temperature ×24 hours +60℃×3 hours +80℃×2 hours;


          4. Note:

          1. Stir well in the packaging bucket before use, or pour out all the resin in the packaging bucket and stir well before use.

          2. The transportation shall comply with the transportation and loading provisions of chemical dangerous goods in Chapter 5 of the Regulations on the Safety Administration of Chemical Dangerous Goods of The State Council. The product should be stored in a cool place below 25℃, avoid fire, isolate heat source, and the shelf life below 25℃ is 3 months.


          5. Product Safety Data (MSDS) :

          Before using this product, be sure to read this product MSDS in detail.

          Hotline

          0523-86925111

          Address: No.1 Yuxing Road, Yonganzhou Town, Gaogang District, Taizhou City

          E-mail:trtuhongyuan@tztrchem.cn

          Follow Us

          Preview mobile website

          Copyright ? 2023 Taizhou Tianrun Synthetic Chemical Co., Ltd

          蘇ICP備18051636號-1 Technical support:MUZINFO
          亚洲中文欧美日韩在线不卡_亚洲精品第一av_2020av天堂网手机在线观看_亚洲av无码之国产精品_国产黄色激情在线观看_久久久久久精品成人自慰无码